BBI 451189 Partially Threaded Cap Screw, 1-8, 10 in L Under Head, 8 Grade, Alloy Steel, Plain
BBI 451189 Partially Threaded Cap Screw, 1-8, 10 in L Under Head, 8 Grade, Alloy Steel, Plain
-
BrandBBI
-
UPC662403654596
-
Manufacturer Part Number451189
-
CountryUSA
-
FinishPlain
-
Tensile Strength150000 psi
-
MaterialAlloy Steel
-
Material SpecificationSAE J429
-
Thread TypeUNC
-
Measurement SystemImperial
-
TypePartially Threaded
-
Grade8
-
Hardness33 to 39 HRC
-
Head Size39/64 in H
-
Head TypeHex
-
Shank Size1 in
-
Diameter - Thread Size1-8
-
Length Under Head10 in
-
UNSPSC31161501
-
Package Description10/CS
-
Standards/ApprovalsANSI B18.2.1-1996
Recently Viewed
BBI 451189 Partially Threaded Cap Screw, 1-8, 10 in L Under Head, 8 Grade, Alloy Steel, Plain
BBI 451189 Partially Threaded Cap Screw, 1-8, 10 in L Under Head, 8 Grade, Alloy Steel, Plain
Due to prolonged, heavy use some components may need to be replaced.
Armstrong® 11-852 Crowfoot Wrench, 1/2 in Open End Wrench, 3/8 in Drive, 1.38 in OAL, ASME B107.21, Polished Chrome
Armstrong® 11-852 Crowfoot Wrench, 1/2 in Open End Wrench, 3/8 in Drive, 1.38 in OAL, ASME B107.21, Polished Chrome
MORSE® 59079 5989 Regular Length Single End Drill Mill, 3/16 in Dia, 60 deg Point, 2 Flutes, 5/8 in L Flute, 5/8 in L of Cut, 3/16 in Dia Shank, 2 in OAL, Bright
MORSE® 59079 5989 Regular Length Single End Drill Mill, 3/16 in Dia, 60 deg Point, 2 Flutes, 5/8 in L Flute, 5/8 in L of Cut, 3/16 in Dia Shank, 2 in OAL, Bright
5/16" X 1-1/4" USS Hex Head GR-2 Tap Bolt
BRAZING ALLOY A brazing alloy that is ideal for large and small copper tubing installations. Self-fluxing on copper. Typical applications include: Refrigeration control valves (copper and brass), joining copper wires to rotor bars, electrical connections, radiant heating systems, air conditioning units, hot and cold water lines, and heat exchanges. T-joints, swage joints and sleeves, couplings on return bends and condenser fittings. Sil-Flo is not recommended for ferrous metals such as iron or steel. It is only for copper base metals as an effective economical alternative to copper-silver alloy rods.